GC Initial Zirconium

Highly stable zirconium oxide frameworks are enjoying increased popularity, because they allow the fabrication of delicate substructures. This highlights an added esthetic potential that you can consistently utilize to your benefit when you use GC Initial Zr. The excellent wettability of GC Initial Zr ceramic guarantees a perfect bond with the different zirconium oxide frameworks. After firing, the sensitive margins fit snugly on the coping, even when thicker layers are used.

Thanks to the exact cross-matched coefficients of thermal expansion (CTE) of 9.4x10–6 K-1 (25°C-500° C), long cooling times can be dispensed when you use this ceramic. This not only saves you precious time but protects your work from stress-cracks and fracturing.